Molykote 1000 Paste Dupont Lead And Nickel Free Anti Seize Paste

Product Description

MOLYKOTE 1000 Solid Lubricant Paste

High-Performance Lubricants

Temperature range - 30 Degrees Centigrade to + 650 Degrees Centigrade

MOLYKOTE 1000 Solid lubricant paste APPLICATIONS:

Molykote 1000 is Suitable for bolted joints that are subjected to high temperatures up to 650 Degrees Centigrade and to corrosive effects, and which, after assembling and the initial operation, have to be re-tightened or disconnected. In order to ensure constant pre-stressing forces, uniform and steady coefficients of friction of the lubricant are necessary.

Molykote 1000  is used successfully for cylinder head bolts, nozzle head screws of plastic injection moulding machines, bolted joints in the chemical industry, and also for the tension rings of centrifuges.

MOLYKOTE 1000 Solid lubricant paste FEATURES:

Molykote 1000 Can be used over a wide range of temperature - 30 Degrees Centigrade to + 650 Degrees Centigrade, High load-carrying capacity, Enables non-destructive dismantling. Even after long use at high temperatures Coefficient of friction unchanged in the area of oiled bolts, even after several bolt re-tightening and loosening processes, Good corrosion protection.

MOLYKOTE 1000 Solid lubricant paste COMPOSITION:

Molykote 1000 is a Solid lubricant

Molykote 1000 is a Thicker

Molykote 1000  is a Powdered Metal

Molykote 1000 is a Mineral Oil

MOLYKOTE 1000 TYPICAL PROPERTIES

Color: Brown

Penetration density : ISO 2137 Unworked penetration mm/10 280-310 &  ISO 2811 Density at 20C (68T)

Temperature Resistance :

Service temperature -18 to 1093C

Load-carrying capacity, wear protection, service life

Four-ball tester

Molykote 1000 DIN 51 350 pt.4 Weld load N 4800

Molykote 1000 DIN 51 350 pt.5 Wear scar under 400N load mm 0.08

Frictional force

Molykote 1000 Coefficient of friction

Molykote 1000 Screw test - u thread2 0.13

Molykote 1000 Screw test - u head 0.08

Molykote 1000 Initial break-away torque3 Nm 135